Carbon fiber pultrusion board

1. Xinshuo® carbon fiber pultrusion board is continuously produced by continuous carbon fiber tow and high-performance epoxy resin independently developed by Jiangshan through thermal curing pultrusion molding process. The carbon wire is fully impregnated and the tensile force is uniform. After molding , The board surface is smooth, high straightness, without splitting. Has excellent corrosion resistance, shock resistance and excellent characteristics of flexible materials. Passed GB 50728-2011 safety appraisal, the strength is stable above 2400MPa.

Retail price

0.0

元

Market price

0.0

元

Number of views:

1000

Product serial number

Quantity

Stock:

Category

Back to list



Honors

Details

Parameters

Product Introduction

2. Has multiple production lines, professional technical team, in-depth development of supporting impregnating resin. Carbon plate width 2cm-20cm, thickness 1.2mm-5mm can be customized according to the project.

3. The annual production capacity is 500,000 square meters, and the size can be customized according to customer project requirements: width 20mm-200mm and thickness 1.2mm-5mm; carbon fiber board is mainly used for bending reinforcement of concrete slabs, beams, concrete wall reinforcement, and chimneys , Tunnel, pool reinforcement, etc.

Packaging Specification

Carton packaging conventional 100 meters/roll

Construction Techology

01 positioning pay-off

02 Concrete surface treatment

03 Carbon plate surface

04 Preparation of carbon sheet adhesive

05 Carbon plate coated with carbon plate glue

06 paste carbon fiber board

07 Temporary support of carbon plate

08 Surface protection

Application range

Carbon fiber pultruded plates are mainly used for flexural reinforcement of concrete slabs, beams, concrete wall reinforcement, chimneys, tunnels, and pool reinforcement.

Technical Parameters

Specification	Product grade	Thickness (mm)	Tensile strength (MPa)	Layer shear strength (MPa)	Tensile elastic modulus (MPa)	Elongation at break (%)	Fiber volume content (%)	Tensile bond strength between fiber composites and concrete under upside-down conditions (Mpa)
CXS-1.4	High Strength Ⅰ	1.4	≥2400	≥50	≥1.6×10⁵	≥1.6	≥65	≥2.5,And concrete cohesive failure
CXS-1.4	High Strength Ⅱ	1.4	≥2000	≥40	≥1.4×10⁵	≥1.4	≥55
CXS-2.0	High Strength Ⅰ	2.0	≥2400	≥50	≥1.6×10⁵	≥1.6	≥65
CXS-2.0	High Strength Ⅱ	2.0	≥2000	≥40	≥1.4×10⁵	≥1.4	≥55
CXS-3.0	High Strength Ⅰ	3.0	≥2400	≥50	≥1.6×10⁵	≥1.6	≥65
CXS-3.0	High Strength Ⅱ	3.0	≥2000	≥40	≥1.4×10⁵	≥1.4	≥55